Arqadia 100% Cottoncore Museum Board
Arqadia 100% CottonCore museum board meets the most stringent requirements for conservation framing. Made entirely from cotton fibre which is not acidic and uses an aqueous EVA adhesive with neutral pH. Water soluble extracts are minimal, chloride below 0.5%, sulphate below 0.25%. This board passes the Silver Tarnish Test. |
|
Specifications
- Acid Free
- Accelerated ageing test Tappi T.509 SU68
Unaged =pH 9.2;
100 yrs = pH 7.8; 150 yrs = pH 7.8
200 yrs = pH 7.8 - Made from 100% cotton fibres
- Buffered with calcium carbonate (minimum 3% by weight)
- Aqueous EVA adhesive with neutral pH
- Contains no plasticisers
| Code | Name | Colour | Size (metric) | Size (imperial) | Calliper | Pack Qty | Pack (£) |
| BDACCB0201 | White | ||||||
| 202 6S 5 | CottonCore Museum | Cream | 815 x 1120 | 32.1" x 44.1" | 1500 microns | 5 | £38.75 |
| 203 6S 5 | CottonCore Museum | Off White | 815 x 1120 | 32.1" x 44.1" | 1500 microns | 5 | £38.75 |
| 204 | flaxen | 815 x 1120 | 1500 microns | 5 | £38.75 | ||
| 205 | willow | 815 x 1120 | 1500 microns | 5 | £38.75 | ||
| BDACCB0211 | CottonCore Museum | Black | 815 x 1120 | 32.1" x 44.1" | 1500 microns | 5 | £38.75 |
| 9201 | white | 1630 x 1120 | 1500 microns | 5 | £77.50 | ||
| BDACCB9202 | cream | 1630 x 1120 | 1500 microns | 5 | £77.50 | ||
| 9203 | off white | 1630 x 1120 | 1500 microns | 5 | £77.50 | ||
| 9204 | flaxen | 1630 x 1120 | 1500 microns | 5 | £77.50 | ||
| 9205 | willow | 1630 x 1120 | 1500 microns | 5 | £77.50 | ||
| 9211 | black | 1630 x 1120 | 1500 microns | 5 | £77.50 | ||
| 580201 | white | 815 x 1120 | 2000 microns | 5 | £51.75 | ||
| 580202 | cream | 815 x 1120 | 2000 microns | 5 | £51.75 | ||
| 580203 | off white | 815 x 1120 | 2000 microns | 5 | £51.75 | ||
| 580204 | flaxen | 815 x 1120 | 2000 microns | 5 | £51.75 | ||
| 580205 | willow | 815 x 1120 | 2000 microns | 5 | £51.75 | ||
| 580211 | black | 815 x 1120 | 2000 microns | 5 | £51.75 |